Question

Sodium chloride reaction Aluminum ​

Answer 1

Answer:

thanks for free points

Answer 2

Answer:

Theoretically, nothing would happen. That is, corrosion is a re-dox reaction and without anything that can be reduced you cannot have oxidation. However, in practice this is not so easy to achieve (as the comments above indicate). Considerable work has been done on electroplating of Al in low temperature molten salt baths containing chlorides (to remove the oxide film). I believe that they have figured out how to do this without significant

corrosion. So, I would look at that literature to see how they do it.

Explanation: